UHP 350mm Graphite Electrodes In Electrolysis For Smelting Steel
Tekheniki Parameter
| Paramethara | Karolo | Yuniti | Lintlha tsa UHP 350mm(14”). |
| Nominal Diameter | Electrode | mm(inch) | 350(14) |
| Max Diameter | mm | 358 | |
| Min Diameter | mm | 352 | |
| Bolelele ba Lebitso | mm | 1600/1800 | |
| Max Length | mm | 1700/1900 | |
| Min Length | mm | 1500/1700 | |
| Max Current Density | KA/cm2 | 20-30 | |
| Bokhoni ba ho Jara ba Hona Joale | A | 20000-30000 | |
| Khanyetso e Itseng | Electrode | μΩm | 4.8-5.8 |
| Nnyo | 3.4-4.0 | ||
| Flexural Matla | Electrode | Mpa | ≥12.0 |
| Nnyo | ≥22.0 | ||
| Modulus ea Bacha | Electrode | GPA | ≤13.0 |
| Nnyo | ≤18.0 | ||
| Boima ba Bongata | Electrode | g/cm3 | 1.68-1,72 |
| Nnyo | 1.78-1,84 | ||
| CTE | Electrode | ×10-6/℃ | ≤1.2 |
| Nnyo | ≤1.0 | ||
| Litaba tsa molora | Electrode | % | ≤0.2 |
| Nnyo | ≤0.2 |
TLHOKOMELISO: Tlhokahalo efe kapa efe e ikhethileng mabapi le dimension e ka fanoa.
Sehlahisoa Kereiti
Limaraka tsa li-electrode tsa graphite li arotsoe ka li-electrode tse tloaelehileng tsa graphite (RP), matla a phahameng a graphite electrode (HP), electrode ea matla a phahameng a graphite (UHP).
Haholo-holo Kopo ea Sebōpi sa Motlakase Arc Ho Etsa Litšepe
Li-electrode tsa graphite bakeng sa ho etsa li-account tsa 70-80% ea kakaretso ea li-electrode tsa graphite. Ka ho fetisa motlakase o phahameng le oa hona joale ho electrode ea graphite, arc ea motlakase e tla hlahisoa pakeng tsa ntlha ea electrode le likotoana tsa tšepe tse tla hlahisa mocheso o moholo ho qhibilihisa sekhechana. Mokhoa oa ho qhibiliha o tla ja electrode ea graphite, 'me e tlameha ho nkeloa sebaka kamehla.
UHP graphite electrode e atisa ho sebelisoa indastering ea tšepe nakong ea tlhahiso ea tšepe ea motlakase ea arc (EAF). Mokhoa oa EAF o kenyelletsa ho qhibilihisa litšepe tse setseng ho hlahisa tšepe e ncha. UHP graphite electrode e sebelisetsoa ho etsa arc ea motlakase, e futhumatsang tšepe e setseng ho fihlela e qhibiliha. Mokhoa ona o sebetsa hantle ebile o theko e boima, kaha o lumella tšepe hore e hlahisoe ka potlako le ka bongata.
Pono ea Karolo le Pono ea Moralo oa Sebōpi sa Motlakase sa Arc
Re baetsi ba lihlahisoa tse felletseng le sehlopha sa litsebi.
30% TT esale pele e le tefo e tlase, The 70% balance TT pele ho pepa.
Lihlahisoa tse amanang
-
Lisebelisoa tsa Graphite Electrode Bakeng sa Corundum Refining E...
Teknoloji Parameter Chart 1: Technical Parameter For Small Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9.5≉ 1.55-1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤45.0. ≤2.4 ≤0.3 Np...
-
Soderberg Carbon Electrode Paste bakeng sa Ferroallo...
Tekheniki Parameter Ntho e Tiisitsoeng Electrode Nakong e Fetileng Standard Electrode Peista GF01 GF02 GF03 GF04 GF05 Volatile Flux(%) 12.0-15.5 12.0-15.5 9.5-13.5 11.5-15.5 11.5-15.5 11.5-Compress 0 15. 22.0 21.0 20.0 Resisitivity(uΩm) 65 75 80 85 90 Volume Density(g/cm3) 1.38 1.38 1.38 1.38 1.38 Elongation(%) 5-20 5-20 5-4 30 1%) 6.0 ...
-
High Density Small Diameter Furnace Graphite El...
Teknoloji Parameter Chart 1: Technical Parameter For Small Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9.5≉ 1.55-1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤45.0. ≤2.4 ≤0.3 Np...
-
Kamehla Power Small Diameter Graphite Electrode...
Teknoloji Parameter Chart 1: Technical Parameter For Small Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9.5≉ 1.55-1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤45.0. ≤2.4 ≤0.3 Ke...
-
Furnace Graphite Electrode Small Diameter 75mm ...
Teknoloji Parameter Chart 1: Technical Parameter For Small Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9.5≉ 1.55-1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤45.0. ≤2.4 ≤0.3 Np...
-
Low Sulfur FC 93% Carburizer Carbon Raiser Iro...
Graphite Petroleum Coke (GPC) Sebopeho se Tsitsitseng Carbon(FC) Volatile Matter(VM) Sulphur(S) Ash Nitrogen(N) Hydrogen(H) Mongobo ≥98% ≤1% 0≤0.05% ≤1% ≤0.03%0% ≤0. ≤0.5% ≥98.5% ≤0.8% ≤0.05% ≤0.7% ≤0.03% ≤0.01% ≤0.5% ≥99% ≤0.5% ≤0.03% ≤0.5%0%≤0% ≤0.5% ≤0%. Size: 0-0.50mm, 5-1mm, 1-3mm, 0-5mm, 1-5mm, 0-10mm, 5-10mm, 5-10mm, 10-15mm kapa ka khetho ea bareki Ho paka: 1. Metsi a sa keneleng metsi. .