Chinese Graphite Electrode Manufacturers 450mm Diameter RP HP UHP Graphite Electrodes
Tekheniki Parameter
| Paramethara | Karolo | Yuniti | RP 450mm(18”) Lintlha |
| Nominal Diameter | Electrode | mm(inch) | 450 |
| Max Diameter | mm | 460 | |
| Min Diameter | mm | 454 | |
| Bolelele ba Lebitso | mm | 1800/2400 | |
| Max Length | mm | 1900/2500 | |
| Min Length | mm | 1700/2300 | |
| Max Current Density | KA/cm2 | 13-17 | |
| Bokhoni ba ho Jara ba Hona Joale | A | 22000-27000 | |
| Khanyetso e Itseng | Electrode | μΩm | 7.5-8.5 |
| Nnyo | 5.8-6.5 | ||
| Flexural Matla | Electrode | Mpa | ≥8.5 |
| Nnyo | ≥16.0 | ||
| Modulus ea Bacha | Electrode | GPA | ≤9.3 |
| Nnyo | ≤13.0 | ||
| Boima ba Bongata | Electrode | g/cm3 | 1.55-1,64 |
| Nnyo | ≥1.74 | ||
| CTE | Electrode | ×10-6/℃ | ≤2.4 |
| Nnyo | ≤2.0 | ||
| Litaba tsa molora | Electrode | % | ≤0.3 |
| Nnyo | ≤0.3 |
TLHOKOMELISO: Tlhokahalo efe kapa efe e ikhethileng mabapi le dimension e ka fanoa.
Molaoli oa Boleng ba Bokaholimo
- Mefokolo kapa masoba ha ea lokela ho feta likarolo tse peli holim'a graphite eleketrode holim'a metsi, 'me mefokolo kapa boholo ba masoba ha bo lumelloe ho feta data e tafoleng e ka tlase e boletsoeng.
- Ha ho na lepetso le pharollang holim'a sebaka sa elektrode. Bakeng sa ho phatloha ha longitudinal, bolelele ba eona ha boa lokela ho ba ho feta 5% ea sedikadikwe sa electrode ea graphite, bophara ba eona e lokela ho ba ka har'a mefuta e fapaneng ea 0.3-1.0mm.Longitudinal crack data e ka tlase ho 0.3mm data e lokela ho ba e fokolang.
- Bophara ba sebaka se seholo sa elektrode ea graphite ha sea lokela ho ba ka tlase ho 1/10 ea circumference electrode ea graphite, 'me bolelele ba sebaka se makukuno (botšo) bo fetang 1/3 ea bolelele ba graphite electrode ha se joalo. dumelloa.
Lintlha tsa Sekoli sa Bokaholimo bakeng sa Graphite Electrode
| Nominal Diameter | Data e nang le bothata(mm) | ||
| mm | intshi | Diameter(mm) | Botebo(mm) |
| 300-400 | 12-16 | 20–40 | 5–10 |
| 450-700 | 18-24 | 30–50 | 10–15 |
Lihlahisoa tse amanang
-
Li-electrode tsa Graphite li Sebelisa Ho Etsa Litšepe Ka Nippl...
Tekheniki Parameter Parameter Karolo Unit RP 500mm(20”) Data Nominal Diameter Electrode mm(inch) 500 Max Diameter mm 511 Min Diameter mm 505 Nominal Length mm 1800/2400 Max Length mm 1900/2500 Min Length mm 1700/230 Delete ea hona joale /cm2 13-16 Hona joale Capacity A 25000-32000 Specific Resistance Electrode μΩm 7.5-8.5 Nipple 5.8-6.5 Flexur...
-
High Purity Sic Silicon Carbide Crucible Graphi...
Silicon Carbide Crucible Performance Parameter Data Data Parameter Data SiC ≥85% Cold Crushing Strength ≥100MPa SiO₂ ≤10% Porosity e Bonahalang ≤%18 Fe₂O₃ <1% Temperature Resistance ≥1200° Resistance Resistance ≥1200 ° Bulk Density6 ≥1200° C. hlahisa ho latela tlhoko ea bareki
-
Lisebelisoa tsa Graphite Electrode Bakeng sa Corundum Refining E...
Teknoloji Parameter Chart 1: Technical Parameter For Small Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9.5≉ 1.55-1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤45.0. ≤2.4 ≤0.3 Np...
-
Small Diameter Graphite Electrodes Rod For Elec...
Teknoloji Parameter Chart 1: Technical Parameter For Small Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.9.5≉ 1.55-1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≤45.0 ≤45.0 ≤45.0. ≤2.4 ≤0.3 Np...
-
UHP 700mm Graphite Electrode Lerge Diameter Gra...
Tekheniki Parameter Parameter Karolo Unit UHP 700mm(28”) Data Nominal Diameter Electrode mm(inch) 700 Max Diameter mm 714 Min Diameter mm 710 Nominal Length mm 2200/2700 Max Length mm 2300/2800 Min Length mm 2100/260 Densi /cm2 18-24 Hona joale Capacity A 73000-96000 Specific Resistance Electrode μΩm 4.5-5.4 Nipple 3.0-3.6 Flexu...
-
Silicon Graphite Crucible For Metal Melting Cla...
Tekheniki Parameter For Clay Graphite Crucible SIC C Modulus of Rupture Temperature Resistance Bulk Density Apparent Porosity ≥ 40% ≥ 35% ≥10Mpa 1790℃ ≥2.2 G/CM3 ≤15% Hlokomela: ho latela tlhoko ea bareki. Tlhaloso Hangata graphite e sebelisitsoeng ho li-crucibles e etsoa ...